Semiconductor device and method for fabricating same

ABSTRACT

A semiconductor device and method for fabricating the same which improves reliability of the semiconductor device is disclosed. The semiconductor device includes: a first insulating film and a gate electrode sequentially formed on a part of a semiconductor substrate; a first insulating spacer formed at both sides above the gate electrode; a second insulating spacer formed at both sides below the gate electrode; and a cobalt silicide film formed on a surface of the gate electrode at a predetermined depth. The method for fabricating the semiconductor device includes the steps of: forming a first insulating film having a hole to expose a part of a semiconductor substrate; forming a second insulating film on the exposed semiconductor substrate inside the hole; forming a gate electrode on the second insulating film to protrude more than the first insulating film; forming a first insulating spacer at both sides of an upper part of the protruded gate electrode; forming a cobalt silicide on a surface of the upper part of the gate electrode; and selectively removing the first insulating film to remain on both sides of a lower part of the gate electrode, so that a second insulating spacer is formed.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a semiconductor device, and more particularly, to a semiconductor device and method for fabricating the same which improves reliability of the semiconductor device.

[0003] 2. Background of the Related Art

[0004] Generally, with high packing density of a semiconductor device, the size of a gate electrode is gradually reduced in the semiconductor device. Accordingly, specific resistance of the gate electrode increases, thereby reducing operation speed of the device.

[0005] In this respect, a manufacture of a gate electrode having low resistivity is essentially required. To this end, a refractory metal silicon of low resistance is used as the gate electrode and it is called a policide(silicide on doped polycrystalline-Si).

[0006] A tungsten silicide WSi₂ having a resistivity value of 60˜200 μΩcm has been widely used, but cobalt silicide (CoSi₂) having a resistivity of 15˜20 μΩcm has recently received much attention, with high packing density of the device.

[0007] However, it is difficult to etch the cobalt silicide (CoSi₂) and thus it is difficult to pattern it. For this reason, the cobalt silicide (CoSi₂) is difficult to be applied to the policide.

[0008] A related art semiconductor device and method for fabricating the same will be described with the accompanying drawings.

[0009] FIGSs. 1 a to 1 f are sectional views showing fabricating process steps of the related art semiconductor device.

[0010] In a structure of the related art semiconductor device, as shown in FIG. 1f, a gate electrode 13 a is formed on a part of a semiconductor substrate 11 and a gate oxide film 12 is interposed between the gate electrode 13 a and the semiconductor substrate 11. An insulating spacer 14 is formed at both sides of the gate oxide film 12 and the gate electrode 13 a. A cobalt silicide film 17 is formed on a surface of the gate electrode 13 a at a predetermined depth.

[0011] A method for fabricating the aforementioned related art semiconductor device will be described below.

[0012] A device isolation region is formed by local oxidation of silicon (LOCOS) process or shallow trench isolation (STI) process to define an active region and an inactive region (not shown) in the semiconductor substrate 11.

[0013] As shown in FIG. 1a, the gate oxide film 12 is formed on the semiconductor substrate 11 of the active region, and a polysilicon film 13 for gate electrode on which impurity ions are doped is deposited on the gate oxide film 12.

[0014] Subsequently, as shown in FIG. 1b, the polysilicon film 13 and the gate oxide film 12 are selectively removed by photolithography and etching processes to form the gate electrode 13 a on the gate oxide film 12.

[0015] A first nitride film is deposited along the surfaces of the semiconductor substrate 11 and the gate electrode 13 a. Then, as shown in FIG. 1c, the first nitride film is selectively removed by anisotropic dry-etching process to remain on both sides of the gate electrode 13 a and the gate oxide film 12, so that the insulating spacer 14 is formed.

[0016] As shown in FIG. 1d, a second nitride film 15 is deposited on an entire surface of the semiconductor substrate 11 including the gate electrode 13 a. At this time, instead of the nitride films such as the first and second nitride films, oxide films may be used.

[0017] As shown in FIG. 1e, the second nitride film 15 is polished by chemical mechanical polishing (CMP) process to expose the surface of the gate electrode 13 a.

[0018] Subsequently, a cobalt film 16 is deposited on the entire surface of the semiconductor substrate 11 including the exposed gate electrode 13 a.

[0019] As shown in FIG. 1f, the cobalt silicide (CoSi₂) film 17 is formed on the surface of the gate electrode 13 a at a predetermined depth by annealing process. The cobalt silicide (CoSi₂) film 17 is formed by reacting cobalt of the cobalt film 16 with silicon of the gate electrode 13 a.

[0020] Afterwards, the cobalt film 16 on the second nitride film 15, which remains without reacting with silicon, is removed using H₂SO₄ solution or HCl solution. The second nitride film 15 is then removed using the cobalt silicide film 17 as a mask to expose the semiconductor substrate 11 at both sides of the gate electrode 13 a and the insulating spacer 14.

[0021] Finally, source/drain regions (not shown) are formed in the exposed semiconductor substrate 11 at both sides of the insulating spacer 14 at predetermined depths by impurity ion implantation using the cobalt silicide film 17 as a mask. Thus, the related art semiconductor device is completed.

[0022] However, the related art semiconductor device and method for fabricating the same has several problems.

[0023] In the CMP process for exposing the surface of the gate electrode, the surface of the gate electrode may not be exposed as the CMP process is not completely performed. In this case, the cobalt silicide is not formed. On the other hand, if the CMP process is performed exceedingly, poor lower pattern may be caused. Furthermore, in the etching process of the polysilicon film to pattern the gate electrode, a photolithography process margin is very small. This is likely to cause a poor gate electrode pattern.

SUMMARY OF THE INVENTION

[0024] An object of the invention is to solve at least the above problems and/or disadvantages and to provide at least the advantages described hereinafter.

[0025] Another object of the present invention is to provide a semiconductor device and method for fabricating the same that substantially obviates one or more of the problems due to limitations and disadvantages of the related art.

[0026] Another object of the present invention is to provide a semiconductor device and method for fabricating the same which improves reliability of the semiconductor device.

[0027] Additional advantages, objects, and features of the invention will be set forth in part in the description which follows and in part will become apparent to those having ordinary skill in the art upon examination of the following or may be learned from practice of the invention. The objects and advantages of the invention may be realized and attained as particularly pointed out in the appended claims.

[0028] To achieve at least these objects and other advantages in a whole or in part and in accordance with purposes of the present invention, as embodied and broadly described, a semiconductor device according to the present invention includes: a first insulating film and a gate electrode sequentially formed on a part of a semiconductor substrate; a first insulating spacer formed at both sides above the gate electrode; a second insulating spacer formed at both sides below the gate electrode; and a cobalt silicide film formed on a surface of the gate electrode at a predetermined depth.

[0029] In another aspect, a method for fabricating a semiconductor device according to the present invention includes the steps of: forming a first insulating film having a hole to expose a part of a semiconductor substrate; forming a second insulating film on the exposed semiconductor substrate inside the hole; forming a gate electrode on the second insulating film to protrude more than the first insulating film; forming a first insulating spacer at both sides of an upper part of the protruded gate electrode; forming a cobalt silicide on a surface of the upper part of the gate electrode; and selectively removing the first insulating film to remain on both sides of a lower part of the gate electrode, so that a second insulating spacer is formed.

[0030] It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0031] The invention will be described in detail with reference to the following drawings in which like reference numerals refer to like elements wherein:

[0032]FIGS. 1a to 1 f are sectional views showing fabricating process steps of a related art semiconductor device;

[0033]FIGS. 2a to 2 g are sectional views showing fabricating process steps of a semiconductor device according to the first embodiment of the present invention; and

[0034]FIGS. 3a to 3 g are sectional views showing fabricating process steps of a semiconductor device according to the second embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0035] Reference will now be made in detail to the preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings.

[0036] In a structure of a semiconductor device according to the first embodiment of the present invention, as shown in FIG. 2g, an oxide film 22 having a hole to expose a part of a semiconductor substrate 21 is formed on the semiconductor substrate 21, and a gate oxide film 25 is formed on the semiconductor substrate 21 inside the hole at a thickness thinner than the oxide film 22. A gate electrode 26 a having a constant height is formed on the gate oxide film 2, and a second insulating spacer 23 a is formed on the oxide film 22 at both sides below the gate electrode 26 a. A first insulating spacer 27 a is formed on the second insulating spacer 23 a at both sides above the gate electrode 26 a, to be connected with the second insulating spacer 23 a. At this time, the first insulating spacer 27 a and the second insulating spacer 23 a have bell shapes. A cobalt silicide (CoSi₂) film 29 is formed on a surface of the gate electrode 26 a at a predetermined depth.

[0037] A method for fabricating the aforementioned semiconductor device according to the first embodiment of the present invention will be described below.

[0038] A device isolation region is formed by LOCOS process or STI process to define an active region and an inactive region (not shown) in the semiconductor substrate 21.

[0039] As shown in FIG. 2a, the oxide film 22 is formed on the semiconductor substrate 21 of the active region, and a first nitride film 23 is deposited on the oxide film 22. The oxide film 22 acts as a buffer during ion implantation for forming source/drain regions.

[0040] Subsequently, as shown in FIG. 2b, the first nitride film 23 and the oxide film 22 are selectively removed by photolithography and etching processes to partially expose the semiconductor substrate 21, so that a gate formation region 24 is defined.

[0041] As shown in FIG. 2c, the gate oxide film 25 is formed on a surface of the exposed semiconductor substrate 21. At this time, the gate oxide film 25 is thinner than the oxide film 22.

[0042] A polysilicon film 26 is deposited on the entire surface of the semiconductor substrate 21 including the first nitride film 23.

[0043] Then, as shown in FIG. 2d, the polysilicon film 26 is selectively removed by photolithography and etching processes to remain on the gate formation region 24 only, so that the gate electrode 26 a is formed. The gate electrode 26 a is aligned in one direction together with the gate oxide film 25.

[0044] A second nitride film 27 is then deposited along the surfaces of the gate electrode 26 a and the first nitride film 23. At this time, instead of the second nitride film, an oxide film may be used.

[0045] As shown in FIG. 2e, the second nitride film 27 is removed by anisotropic dry-etching process to remain on both sides of the gate electrode 26 a, so that the first insulating spacer 27 a is formed.

[0046] A cobalt film 28 is then deposited along the surfaces of the first nitride film 23, the first insulating spacer 27 a and the gate electrode 26 a.

[0047] As shown in FIG. 2f, a cobalt silicide ((CoSi₂) film 29 is formed on the surface of the gate electrode 26 a at a predetermined depth by annealing process. The cobalt silicide (CoSi₂) film 29 is formed by reacting cobalt of the cobalt film 28 with silicon of the gate electrode 26 a.

[0048] Afterwards, the cobalt film 28 which remains without reacting with silicon is removed using H₂SO₄ solution or HCl solution.

[0049] As shown in FIG. 2g, the first nitride film 23 is selectively removed to remain on both sides of the gate electrode 26 a, so that the second insulating spacer 23 a is formed at both sides of the gate electrode 26 a below the first insulating spacer 27 a.

[0050] Finally, source/drain regions(not shown) are formed in the semiconductor substrate 21 at predetermined depths by impurity ion implantation using the cobalt silicide film 29 as a mask. Thus, the semiconductor device according to the first embodiment of the present invention is completed.

[0051] Now, a method for fabricating a semiconductor device according to the second embodiment of the present invention will be described. In the second embodiment of the present invention, a photolithography process margin is improved in patterning the gate electrode.

[0052] In a structure of the semiconductor device according to the second embodiment of the present invention, as shown in FIG. 3g, a first oxide film 32 having a hole to expose a part of a semiconductor substrate 31 is formed on the semiconductor substrate 31, and a gate electrode 37 a which is aligned with the hole is formed on the exposed semiconductor substrate 31. A third insulating spacer 33 a is formed at both sides below the gate electrode 37 a, and a second insulating spacer 38 a is formed on the third insulating spacer 33 a at both sides above the gate electrode 37 a, to be connected with the third insulating spacer 33 a. At this time, the second insulating spacer 38 a and the third insulating spacer 33 a have bell shapes. A first insulating spacer 35 a is formed at a side inside the hole of the third insulating spacer 33 a, and a gate oxide film 36 is formed on the semiconductor substrate 31 inside the hole at a side of the first insulating spacer 35 a. The gate oxide film 36 is thinner than the first oxide film 32.

[0053] The method for fabricating the aforementioned semiconductor device according to the second embodiment of the present invention will be described below.

[0054] A device isolation region is formed by LOCOS process or STI process to define an active region and an inactive region (not shown) in the semiconductor substrate 31.

[0055] As shown in FIG. 3a, the first oxide film 32 is formed on the semiconductor substrate 31 of the active region, and a first nitride film 33 is deposited on the first oxide film 32. The first oxide film 32 acts as a buffer during ion implantation for forming source/drain regions.

[0056] Subsequently, as shown in FIG. 3b, the first nitride film 33 and the first oxide film 32 are selectively removed by photolithography and etching processes to partially expose the semiconductor substrate 31, so that a gate formation region 34 is defined. The second oxide film 35 is then deposited along a surface of the first nitride film 33.

[0057] As shown in FIG. 3c, the second oxide film 35 is removed by anisotropic dry-etching process to remain on both sides of the first nitride film 33 inside the gate formation region 34, so that the first insulating spacer 35 a is formed.

[0058] Subsequently, the gate oxide film 36 is formed on a surface of the exposed semiconductor substrate 31. At this time, the gate oxide film 36 is thinner than the first oxide fin 32.

[0059] A polysilicon film 37 is deposited on the entire surface of the semiconductor substrate 31 including the first nitride film 33.

[0060] Then, as shown in FIG. 3d, the polysilicon film 37 on the first nitride film 33 is removed by photolithography and etching processes to remain on the gate formation region 34 only, so that the gate electrode 37 a is formed on the gate oxide film 36. The gate electrode 37 a is aligned in one direction together with the gate formation region 34.

[0061] A second nitride film 38 is then deposited along the surfaces of the gate electrode 37 a and the first nitride film 33. At this time, instead of the second nitride film 38, an oxide film may be used.

[0062] As shown in FIG. 3e, the second nitride film 38 is selectively removed by anisotropic dry-etching process to remain on both sides of the gate electrode 37 a, so that the second insulating spacer 38 a is formed.

[0063] A cobalt film 39 is then deposited along the surfaces of the first nitride film 33, the second insulating spacer 38 a and the gate electrode 37 a.

[0064] As shown in FIG. 3f, a cobalt silicide (CoSi₂) film 40 is formed on the surface of the gate electrode 37 a at a predetermined depth by annealing process. The cobalt silicide (CoSi₂) film 40 is formed by reacting cobalt of the cobalt film 39 with silicon of the gate electrode 37 a.

[0065] Afterwards, the cobalt film 39 which remains without reacting with silicon is removed using H₂SO₄ solution or HCl solution.

[0066] As shown in FIG. 3g, the first nitride film 33 is selectively removed to remain on both sides of the gate electrode 37 a, so that the third insulating spacer 33 a is formed.

[0067] Finally, source/drain regions(not shown) are formed in the semiconductor substrate 31 at predetermined depths by impurity ion implantation using the cobalt silicide film 40 as a mask. Thus, the semiconductor device according to the second embodiment of the present invention is completed.

[0068] As aforementioned, the aforementioned semiconductor device and method for fabricating the same according to the present invention has the following advantages.

[0069] First, since the policide gate is formed without CMP process, any error caused by the CMP process is avoided, thereby improving reliability of the device. Furthermore, it is possible to improve a photolithography process margin during patterning process of the gate electrode by forming the insulating spacer inside the hole after etching the nitride film.

[0070] The foregoing embodiments and advantages are merely exemplary and are not to be construed as limiting the present invention. The present teaching can be readily applied to other types of apparatuses. The description of the present invention is intended to be illustrative, and not to limit the scope of the claims. Many alternatives, modifications, and variations will be apparent to those skilled in the art. In the claims, means-plus-function clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents but also equivalent structures. 

What is claimed is:
 1. A semiconductor device comprising: a first insulating film and a gate electrode sequentially formed on a part of a semiconductor substrate; a first insulating spacer formed at both sides above the gate electrode; a second insulating spacer formed at both sides below the gate electrode; and a cobalt silicide film formed on a surface of the gate electrode at a predetermined depth.
 2. The semiconductor device of claim 1, further comprising a third insulating spacer formed at a side of the second insulating spacer in the interface between the second insulating spacer and the gate electrode.
 3. The semiconductor device of claim 1, further comprising a second insulating film formed on the semiconductor substrate on which the first insulating film is not formed, at a thickness thicker than the first insulating film.
 4. The semiconductor device of claim 1, wherein the first insulating spacer is either an oxide film or a nitride film.
 5. The semiconductor device of claim 1, wherein the second insulating spacer is a nitride film.
 6. The semiconductor device of claim 1, wherein the first insulating film is an oxide film.
 7. The semiconductor device of claim 1, wherein the second insulating spacer is connected with the first insulating spacer to have a bell shape.
 8. The semiconductor device of claim 3, wherein the second insulating film is an oxide film.
 9. A method for fabricating a semiconductor device comprising the steps of: forming a first insulating film having a hole to expose a part of a semiconductor substrate; forming a second insulating film on the exposed semiconductor substrate inside the hole; forming a gate electrode on the second insulating film to have a height higher than the first insulating film; forming a first insulating spacer at both sides of an upper part of the protruded gate electrode; forming a cobalt silicide on a surface of the upper part of the gate electrode; and selectively removing the first insulating film to remain on both sides of a lower part of the gate electrode, so that a second insulating spacer is formed.
 10. The method of claim 9, wherein the first insulating film and the second insulating spacer arc nitride films.
 11. The method of claim 9, wherein the second insulating film is an oxide film.
 12. The method of claim 9, wherein the first insulating spacer is either a nitride film or an oxide film.
 13. The method of claim 9, further comprising the step of forming a third insulating spacer at both sides of the first insulating film inside the hole after forming the hole.
 14. The method of claim 9, wherein the cobalt silicide is formed by depositing cobalt on an entire surface of the semiconductor substrate including the gate electrode and performing annealing.
 15. The method of claim 9, wherein the remaining cobalt is removed using H₂SO₄ solution or HCl solution after forming the cobalt silicide.
 16. The method of claim 9, further comprising the step of forming source/drain regions in the semiconductor substrate at both sides of the second insulating spacer at predetermined depths by impurity ion implantation using the cobalt silicide as a mask, after forming the second insulating spacer.
 17. The method of claim 9, wherein the first and second insulating spacers are formed by anisotropic dry-etching process.
 18. The method of claim 9, further comprising the step of a third insulating film on the semiconductor substrate at an etching ratio different from that of the first insulating film, before forming the first insulating film.
 19. The method of claim 13, wherein the third insulating spacer is an oxide film.
 20. The method of claim 18, wherein the third insulating film is an oxide film. 